Study on microwave absorbing properties of multi-walled carbon nanotubes
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    用石蜡分别与多壁碳纳米管及大内径薄多壁碳纳米管按不同的质量比混合,制得了复合吸波材料.采用同轴法测量了复合材料在2~18 GHz范围内的复介电常数和复磁导率,并计算了材料对微波的反射率,分析了其吸波性能.结果表明:碳纳米管复合材料在2~18 GHz范围具有吸波性能.其中质量分数为15%的多壁碳纳米管的最大吸收峰在10.4 GHz,其值为-21.7 dB,质量分数为15%的大内径薄壁多壁碳纳米管的最大吸收峰在11.2 GHz,值为-17.6 dB.

    Abstract:

    Multi-walled carbon nanotubes and large inner diameter-thin walled carbon nanotubes were respectively combined with paraffin wax in different mass ratio to prepare microwave absorption composites.The complex permittivity and permeability of the composites were measured,and the reflectivity of electromagnetic waves was calculated.The results show that maximum absorption of the multi-walled carbon nanotubes is about -21.7 dB at 10.4 GHz,and that of the Large Inner Diameter-thin walled Carbon Nanotubes is -17.6 dB at 11.2 GHz.

    参考文献
    相似文献
    引证文献
引用本文

沈国柱,虞超,马荣,程国生.多壁碳纳米管复合材料的微波吸收性能[J].南京信息工程大学学报(自然科学版),2012,4(5):461-465
SHEN Guozhu, YU Chao, MA Rong, CHENG Guosheng. Study on microwave absorbing properties of multi-walled carbon nanotubes[J]. Journal of Nanjing University of Information Science & Technology, 2012,4(5):461-465

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2011-06-07
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期:

地址:江苏省南京市宁六路219号    邮编:210044

联系电话:025-58731025    E-mail:nxdxb@nuist.edu.cn

南京信息工程大学学报 ® 2024 版权所有  技术支持:北京勤云科技发展有限公司